In an article recently published in the journal ACS Applied Energy Materials, researchers discussed the utility of gadolinium fluoride (GdF3) as an electron-selective contact material for the development of solar cells with a high thickness tolerance.
Study: Gadolinium Fluoride as a High-Thickness-Tolerant Electron-Selective Contact Material for Solar Cells . Image Credit: Thongsuk7824/Shutterstock.com
Solar cells made of crystalline silicon (c-Si) account for the vast bulk of the market. Due to their higher efficiency and low mass production, the photovoltaic industry has progressed from aluminum back-surface-field (Al-BSF) c-Si solar cells to rear cells and passivated emitters.
Traditional c-Si solar cells have low efficiency due to substantial recombination loss in Al-BSF3 and a high-temperature diffused p-n junction. A significant aspect in achieving c-Si solar cells with high efficiency is strong carrier selectivity. Thin heavily/intrinsic doped and hydrogenated amorphous silicon (a-Si/H) layers and ultrathin heavily doped/tunnel oxide poly-Si layers have a band-gap (Eg) wider than c-Si, demonstrating excellent carrier selectivity and efficiency.
The short-circuit current density (Jsc) will drop if the film thickness is not precisely controlled. The doping of these thin films also necessitates a high level of expertise and expensive equipment. Because of all these issues, mass production of such heterojunction solar cells is prohibitively expensive.
Due to its advantages of simplifying the preparation process and lowering intrinsic loss, a dopant-free carrier-selective contact (DFCSC) has been incorporated into the manufacturing of c-Si solar cells in recent years. Transition-metal oxides, including as NiOx, V2Ox, WOx, and MoOx have been extensively studied as dopant-free hole selective materials.
In this study, the authors presented the development of GdF3 having a low work function, which was used to produce a low contact resistivity (ρc) Ohmic contact with lightly doped n-type c-Si (n-Si). The dopant-less GdF3/Al electron-selective contact is applied to n-Si solar cells with partial rear contact designs, and the corresponding power conversion efficiency (PCE) was estimated.
The researchers used GdF3 as a new dopant-free electron-selective contact material. Thermal evaporation was used to deposit GdF3 and Al films from powder and wire, respectively, under a high background vacuum. A crystal oscillator was used to monitor the GdF3 and Al deposition process, and ex situ spectroscopic ellipsometry was used to calibrate the thickness of GdF3 layers. Czochralski (Cz) n-Si wafers with sufficient resistivity were employed as substrates. For good sample conductivity, 5 nm GdF3 was coated on low-resistivity (0.05-0.1 Ωcm) polished silicon wafers for photoelectron spectroscopy characterization.
The team utilized X-ray photoelectron spectroscopy (XPS) to determine the composition and chemical state of the thin film formed on n-Si by thermal evaporation from GdF3 powder (99.99%). The transfer length method (TLM) was used to determine the contact resistivity of the n-Si (1-3 Ωcm)/GdF3/Al structure.
The low c for the GdF3/Al stack was replicated and showed good stability in an ambient atmosphere over a wide thickness variation (1.4-5.6 nm). The contact resistivity average and maximum values in this region were roughly 10 mΩ cm2 and less than 45 mΩ cm2, respectively.
Even after 1000 hours of exposure in air, the average contact resistivity values for samples with GdF3 layers between 1.4 and 5.6 nm were still less than 75 mΩ cm2. Furthermore, the interface picture and elemental distribution revealed Al diffusion into the GdF3 layer, which was attributed to its high thickness tolerance. The dopant-less GdF3/Al electron-selective contact applied to n-Si solar cells with partial rear contact designs obtained a high PCE of 20.71%, which revealed its enormous potential for mass production of optical and electrical devices.
More from AZoM: What is Femtosecond Laser-Based 3D Printing?
The XPS data revealed that the GdF3 film formed by thermal evaporation was stoichiometric. According to the ultraviolet photoelectron spectroscopy (UPS) measurements, the thin film material had an ultralow work function (ϕ = 2.85 eV). The results of high-resolution transmission electron microscopy (HRTEM) demonstrated that Al was diffused into the GdF3 layer and subsequently formed a mixing layer. The dispersed Al facilitated the electron transportation and explained the structure's high thickness tolerance. Proof-of-concept cells with a partial back contact architecture attained a PCE of 20.71%. However, cells with GdF3 thicknesses ranging from 1.4 to 5.6 nm had a PCE of around 20%.
F-1s of metal fluorides were found responsible for the peak at a binding energy of 685.19 eV. Gd 3d5/2 and F-1s had a relative sensitivity factor of 1:3.02. The thin film's valence band maximum was 5.3 eV lower than the Fermi level. After the GdF3 layer was inserted, the fill factor (FF) increased from 68.8 to 77.5%, and the open-circuit voltage (Voc) climbed from 621 to 652 mV. As a result, the cell's PCE improved from 17.40 to 20.71%.
In conclusion, this study elucidated that in a reasonably wide thickness range of 1.4 to 5.6 nm, the low contact resistivity, ρc (<2 mΩ cm2) of the GdF3/Al structure showed a mild thickness dependence. Diffusion and the mixing of Al were found responsible for the relatively high thickness tolerance of contact resistivity. A PCE of 20.71% was observed for the proof-of-concept solar cell.
The authors emphasized that GdF3 can be a promising dopant-free electron-selective contact material for low-cost and efficient solar cells. They also indicated that the impact of metal deposition rates and the possibility of an Al-GdF3 reaction will be investigated further.
Chen, N., Cai, L., Xie, F., et al. Gadolinium Fluoride as a High-Thickness-Tolerant Electron-Selective Contact Material for Solar Cells. ACS Applied Energy Materials (2022). https://pubs.acs.org/doi/10.1021/acsaem.1c03919
Disclaimer: The views expressed here are those of the author expressed in their private capacity and do not necessarily represent the views of AZoM.com Limited T/A AZoNetwork the owner and operator of this website. This disclaimer forms part of the Terms and conditions of use of this website.
Surbhi Jain is a freelance Technical writer based in Delhi, India. She holds a Ph.D. in Physics from the University of Delhi and has participated in several scientific, cultural, and sports events. Her academic background is in Material Science research with a specialization in the development of optical devices and sensors. She has extensive experience in content writing, editing, experimental data analysis, and project management and has published 7 research papers in Scopus-indexed journals and filed 2 Indian patents based on her research work. She is passionate about reading, writing, research, and technology, and enjoys cooking, acting, gardening, and sports.
Please use one of the following formats to cite this article in your essay, paper or report:
Jain, Surbhi. (2022, March 24). The Role of Gadolinium Fluoride in Solar Cells. AZoM. Retrieved on May 21, 2022 from https://www.azom.com/news.aspx?newsID=58623.
Jain, Surbhi. "The Role of Gadolinium Fluoride in Solar Cells". AZoM. 21 May 2022. <https://www.azom.com/news.aspx?newsID=58623>.
Jain, Surbhi. "The Role of Gadolinium Fluoride in Solar Cells". AZoM. https://www.azom.com/news.aspx?newsID=58623. (accessed May 21, 2022).
Jain, Surbhi. 2022. The Role of Gadolinium Fluoride in Solar Cells. AZoM, viewed 21 May 2022, https://www.azom.com/news.aspx?newsID=58623.
Do you have a review, update or anything you would like to add to this news story?
AZoM speaks with Dr. Nicola Ferralis from MIT about his research that has developed a low-cost process of creating carbon fibers from hydrocarbon pitch. This research could lead to the large-scale use of carbon fiber composites in industries that have thus far been limited.
In this interview, AZoM speaks with Marco Enger, Senior Tribologist from GGB, to discuss how nano fillers affect transfer films within tribological systems.
Ahead of their talk on green chemistry and profitability in laboratory research at ChemUK 2022, AZoM spoke with Jacqueline Balian from Gambica and Martyn Fordman from Asynt about encouraging sustainability in the chemical industry.
COXEM's CP-8000+ is a powerful cross section polishing tool that uses an argon ion beam to allow precise, advanced sample preparation. Its state-of-the-art technology means the sample is not deformed and does not suffer any kind of physical damage.
This product profile outlines the background information of ARSST tool that is being used for screening tests and operating in "open cell" mode.
This product profile outlines the Evolution™ Pro UV-Vis Spectrophotometers from Thermo Fisher Scientific.
This article provides an end-of-life assessment of lithium-ion batteries, focusing on the recycling of an ever-growing amount of spent Li-Ion batteries in order to work toward a sustainable and circular approach to battery use and reuse.
Corrosion is the degradation of an alloy caused by its exposure to the environment. Corrosion deterioration of metallic alloys exposed to the atmosphere or other adverse conditions is prevented using a variety of techniques.
Due to the ever-increasing demand for energy, the demand for nuclear fuel has also increased, which has further created a significant increase in the requirement for post-irradiation examination (PIE) techniques.
AZoM.com - An AZoNetwork Site
Owned and operated by AZoNetwork, © 2000-2022